Refractory Technology Presence of MgO in alumino-silicate refractories __________ its refractoriness. Increases Lowers Either A or B; depends on its quantity Does not affect Increases Lowers Either A or B; depends on its quantity Does not affect ANSWER DOWNLOAD EXAMIANS APP
Refractory Technology Fireclay bricks are used in the Flues Chimney linings Furnaces allowed to cool frequently All of these Flues Chimney linings Furnaces allowed to cool frequently All of these ANSWER DOWNLOAD EXAMIANS APP
Refractory Technology Bauxite calcining rotary kilns are lined with __________ bricks. Fireclay Carbon 85% alumina Corundum Fireclay Carbon 85% alumina Corundum ANSWER DOWNLOAD EXAMIANS APP
Refractory Technology Refractoriness of a typical silica brick corresponds to Segar cone number, '32', which is equivalent to a temperature of __________ °C. 1915 1710 1380 1520 1915 1710 1380 1520 ANSWER DOWNLOAD EXAMIANS APP
Refractory Technology Silliminite (Al2O₃.SiO₂) refractory, which is a neutral refractory, is not used in Gas retorts Pottery furnace Crucibles Glass melting furnace Gas retorts Pottery furnace Crucibles Glass melting furnace ANSWER DOWNLOAD EXAMIANS APP
Refractory Technology Magnesite chrome refractories Have better spalling resistance than chrome magnesite refractories Have very low (50 kg/cm² ) cold crushing strength (C.C.S.), and can not be used in metalcase form Have very low thermal co-efficient of expansion Are not at all resistant to the corrosive action of iron oxide Have better spalling resistance than chrome magnesite refractories Have very low (50 kg/cm² ) cold crushing strength (C.C.S.), and can not be used in metalcase form Have very low thermal co-efficient of expansion Are not at all resistant to the corrosive action of iron oxide ANSWER DOWNLOAD EXAMIANS APP