Refractory Technology Lower part of hot metal mixer are lined with __________ bricks. Silica Superduty fireclay High alumina Carborundum Silica Superduty fireclay High alumina Carborundum ANSWER DOWNLOAD EXAMIANS APP
Refractory Technology Resistance to slag attack of a refractory Decreases at higher temperature Decreases, if defective joints & cracks exist in the refractory All of these Depends on the nature of slag & refractory Decreases at higher temperature Decreases, if defective joints & cracks exist in the refractory All of these Depends on the nature of slag & refractory ANSWER DOWNLOAD EXAMIANS APP
Refractory Technology Which is not a high alumina refractory? Mullite Corrundum Dolomite Bauxite Mullite Corrundum Dolomite Bauxite ANSWER DOWNLOAD EXAMIANS APP
Refractory Technology Upper portion of hot metal mixer are lined with mullite bricks, which helps in resisting the Washing action of metal Corrosion by layer of slag Both A & B Neither A nor B Washing action of metal Corrosion by layer of slag Both A & B Neither A nor B ANSWER DOWNLOAD EXAMIANS APP
Refractory Technology Silica bricks have low spalling resistance below 600°C, due to its High co-efficient of expansion upto this temperature Low refractoriness High thermal diffusivity Very high thermal conductivity High co-efficient of expansion upto this temperature Low refractoriness High thermal diffusivity Very high thermal conductivity ANSWER DOWNLOAD EXAMIANS APP
Refractory Technology Refractoriness under loads (RUL) is quite close to the fusion temperature (PCE) for __________ bricks. Silica Very low alumina Fireclay Dolomite Silica Very low alumina Fireclay Dolomite ANSWER DOWNLOAD EXAMIANS APP